Deutsch| Product | Properties / field of application | Crosslinker type | Crosslinker addition % | Colour of caoutchouc | Density g/cm³ | Mixed viscosity at RT mPas | Pot life at RT min | Time required up to the demouldability hours | Tensile strength DIN 53504 N/mm² | Elongation at break DIN 53504 % | Resistance to tear propagation ASTM D 624 B N/mm | Shore A-hardness DIN 53505 | Data Sheet |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| NEUKASIL RTV 1703 | high resistance to initial tearing and tear propagation, can be made thixotropic, good flow properties, for mould making and artistic casting, suitable for epoxy resins, polyurethanes, wax | 1703 Comp. B1 1703 Comp. B2 SI - C | 5 5 0,1 - 1,0 | white | 1.22 | 24,000 32,000 | 80 15 - | 24 12 - | 4 3.5 - | 800 750 - | >20 >20 - | 23 23 - |  |
| NEUKASIL RTV 102 | good resistance, against resins, low shore hardness, with C 02 S short pot life | C 02 C 02 S | 5 5 | white | 1.1 | 20,000 16,000 | 100 15 | 20 10 | 3.0 2.5 | 450 450 | 20 20 | 21 19 | |
| NEUKASIL RTV 103 | good resistance against resins, medium shore hardness, with C 02 S short pot life | C 02 C 02 S | 5 5 | white | 1.1 | 37,000 48,000 | 90 15 | 20 10 | 2.5 2.5 | 420 420 | 20 20 | 28 26 | |
| Product | Properties / field of application | Crosslinker type | Crosslinker addition % | Colour of caoutchouc | Mixed viscosity at RT mPas | Pot life at RT min | Tack-free in hours | Shore A hardness DIN 53505 (24h) | Shore A hardness DIN 53505 (7d) | Tensile strength N/mm² DIN 53505 S2 | Elongation at break % DIN 53505 S2 | Data Sheet |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| NEUKASIL RTV 125 | high resistance to initial tearing and tear propagationt, one crosslinker each with a good resistance to styrene (C 125 PE) and a good resistance to polyurethane (C 125 PU), can be made thixotropic | C 125 PE C 125 PU SI - C | 5 5 0,1 - 1,5 | Bernstein Creme Transluzent | 25.000 25.000 - | 70 70 - | 26 26 - | 24 24 - | 28 28 - | 3,5 5,5 - | 800 650 - | |
| NEUKASIL SN 1971 | high resistance to initial tearing and tear propagation, very good flow properties mould making | C 02 C 04 NEW | 5 20 | white white | 9,000 4,000 | 95 60 | 24 24 | 13 10 | 15 11 | 3 2 | 370 420 | |