DeutschShore A - 0 to 20 points
| Shore A | Product | Properties / field of application | Crosslinker type | Crosslinker addition % | Colour of caoutchouc | Mixed viscosity at RT mPas | Pot life in min | Demoulding in hours | Data Sheet |
|---|---|---|---|---|---|---|---|---|---|
| 6 | NEUKASIL RTV 23 | standard system, low viscosity, low shore hardness, high elongation | A 7 colorless | 40 | translucent | 3,500 | 150 | 24 |  |
| 6 | NEUKASIL SN 2972 | high resistance to initial tearing and tear propagation, very good flowability, can be made thixotropic | SN 2972 comp. B | 100 | translucent | 2,250 | 20 | 24 | |
| 7 | NEUKASIL RTV 26 | low hardness, very good flowability, good resistance to initial tearing and tear propagation production of products for orthopaedics, suitable for polyester, epoxides, wax, casting of electrical component parts, production of parts, prototypes | A 7 blue | 40 | blue | 7,000 | 200 | 24 | |
| 11 | NEUKASIL SN 2978 | high resistance to initial tearing and tear propagation, very good flowability, can be made thixotropic | SN 2978 comp. B | 100 | translucent | 2,000 | 25 | 16 | |
| 12 | NEUKASIL RTV 23 | standard system, very low viscosity, low shore hardness, high elongation | A 14 colorless | 30 | translucent | 8,500 | 120 | 24 | |
| 15 | NEUKASIL RTV 26 | variable hardness, very good flow properties, high resistance to initial tearing and tear propagation production of elastic moulds, suitable for polyester / gypsum / wax, casting of electrical components, production of orthopaedics, coating of tissues | A 14 colorless | 30 | white | 15,000 | 120 | 24 | |
| 19 | NEUKASIL SN 2953 mod 2 | high resistance to initial tearing and tear propagation, very good flowability, can be made thixotropic | SN 2953 mod. 2 comp. B | 100 | translucent | 2,500 | 11 | 3 | |
Shore A - 20 to 40 points
| Shore A | Product | Properties / field of application | Crosslinker type | Crosslinker addition % | Colour of caoutchouc | Mixed viscosity at RT mPas | Pot life in min | Demoulding in hours | Data Sheet |
|---|---|---|---|---|---|---|---|---|---|
| 20 | NEUKASIL RTV 23 | variable hardness, very good flowability, high resistance to initial tearing and tear propagation, variable pot lives production of elastic moulds, suitable for e.g. plaster / wax, casting of electric component parts, product for orthopaedics, coating of tissues | A 3 colorless | 6.5 | translucent | 30,000 | 60 | 24 | |
| 21 | NEUKASIL SN 2962 | high resistance to initial tearing and tear propagation, very good flowability, can be made thixotropic, fast curing | SN 2962 comp. B | 100 | white or green | 5,000 | 15 | 2 | |
| 21 | NEUKASIL SN 2888 | good resistance to initial tearing and tear propagatoin, very good flowability, can be made thixotropic, quick through-curing general mould making, body cast | SN 2888 comp. B | 100 | translucent | 2,900 | 5 | 0.5 | |
| 22 22 | NEUKASIL RTV 22 | high resistance to initial tearing and tear propagation, very good flowability, can be made thixotropic, quick through-curing general mould making, body cast | A 142 orange A 156 orange A 162 orange | 100 100 100 | orange orange orange | 2,700 2,700 2,700 | 5 30 60 | 0.5 12 18 | |
| 22 | NEUKASIL RTV 22 F | high resistance to initial tearing and tear propagation, very good flowability, can be made thixotropic, quick through-curing general mould making, body cast, production of moulds for chocolate, marzipan and similar | A 142 F orange | 100 | orange | 3,250 | 5 | 0.5 | |
| 25 | NEUKASIL RTV 22 SP | high resistance to initial tearing and tear propagation, sprayable on vertical surfaces, can be made thixotropic, quick through-curing | A 142 SP | 100 | orange | 11,500 | 5 | 0.5 | |
| 25 | NEUKASIL RTV 23 | variable hardness, very good flowability, high resistance to initial tearing and tear propagation, variable pot lives production of elastic moulds, suitable for e.g. plaster / wax, casting of electric component parts, product for orthopaedics, coating of tissues | A 18 colorless or blue | 10 | translucent or blue | 25,000 | 90 | 24 | |
| 28 | NEUKASIL RTV 26 | very good flowability, high resistance to initial tearing and tear propagation production of elastic moulds, suitable for plaster, wax, polyester, casting of electrical component parts, products for orthopaedics, coating of fabrics, compliant with FDA 21 CFR 177.2600 and BfR-Recommendation XV „Silicones“ | A 18 colorless or blue | 10 | colourless or blue | 25,000 | 90 | 24 | |
| 28 | NEUKASIL RTV 230 | high resistance to initial tearing and tear propagation, very good flowability, can be made thixotropic, mixing ratio 1 : 1, quick through-curing general mould making, lifecasting, production of moulds for chocolate, marzipan and similar, compliant with FDA 21 CFR 177.2600 and BfR-Recommendation XV „Silicones“ | A 149 reddish brown/ colorless/orange | 100 | reddish brown/ colorless/orange | 5,000 | 40 | 24 | |
| 30 | NEUKASIL RTV 29 | shore 00 hardness, production of pads for padprinting, very low viscosity | A 99 reddish brown | 5 | reddish brown | 3,000 | 180 | 24 | |
| 37 37 | NEUKASIL SN 2954 | high resistance to initial tearing and tear propagation, very good flowability, can be made thixotropic | SN 2954 comp. B SN 2954 comp. B 1 | 100 100 | translucent/redbrown translucent | 6,200 6,200 | 25 50 | 3 12 | |
| 37 37 | ProtoSil RTV 260 NEW | very good flow properties, shrinkage-free vulcanization at room temperature, can be made thixotropic, high resistance to initial tearing and tear propagation, very high transparence production of elastic moulds, particularly for prototypes, excellent resistance to vacuum casting resins | RTV 260 NEW comp. B1 (dry) RTV 260 NEW comp. B2 (oily) | 100 100 | colorless colorless | 15,000 23,000 | 60 60 | 16 16 | |
| 40 | NEUKASIL RTV 230-7 AS | production of antistatic prefabricated products, addition-crosslinking | B (platinum component) | 10 | grey | 10,000 | 30 | 24 | |
| 40 39 | ProtoSil RTV 245 NEW | Shore hardness A 40, very good flow properties, shrinkage-free vulcanization at room temperature, can be made thixotropic, high resistance to initial tearing and tear propagation, very high transparency production of elastic moulds, particulary for prototypes, excellent resistance to vacuum casting resins | RTV 245 NEW comp. B1 (dry) RTV 245 NEW comp. B2 (oily) | 10 10 | colorless colorless | 35,000 50,000 | 60 60 | 24 24 | |
Shore A > 40 points
| Shore A | Product | Properties / field of application | Crosslinker type | Crosslinker addition % | Colour of caoutchouc | Mixed viscosity at RT mPas | Pot life at RT min | Demoulding in hours | Data Sheet |
|---|---|---|---|---|---|---|---|---|---|
| 45 45 | NEUKASIL RTV 27 | low-viscous, mean Shore hardness, variable pot life general mould making, coating of fabrics, embedding material and material for electrical insulation | A 43 transparent A 108 transparent | 10 10 | transparent transparent | 4,500 4,500 | 60 240 | 24 24 | |
| 45 | NEUKASIL RTV 20 | very good flowability, high Shore A-hardness general mould making, coating of woven fabrics, embedding and electrical insulation | A 101 colorless / blue | 20 | white / grey | 35,000 | 130 | 24 | |
| 55 | NEUKASIL RTV 20 | very good flowability, high resistance to initial tearing and tear propagation, higher Shore A hardness, variable pot life mould making, suitable for polyester, epoxies, wax, casting of electrical component parts, production of parts, prototypes, compliant with FDA 21 CFR 117.2600 and BfR-Recommendation XV „Silicones“ | A 26 colorless / blue | 10 | colorless / blue | 80,000 | 120 | 24 | |
| 55 55 55 | NEUKASIL RTV 20 | very good flowability, high resistance to initial tearing and tear propagation, higher Shore A hardness, variable pot life mould making, suitable for polyester, epoxies, wax, casting of electrical component parts, production of parts, prototypes, compliant with FDA 21 CFR 177.2600 and BfR-Recommendation XV „Silicones“ | A 2 slow colorless / blue A 2 rapid colorless / blue retarder SN 2994 colorless (test in conjunction with crosslinker A 2 rapid) | 10 10 4 | blue / colorless blue / colorless white | 80,000 80,000 80,000 | 90 15 90 | 24 12 24 | |
| 58 | NEUKASIL RTV 25 | very good flowability, high Shore A-hardness, medium-viscous general mould making, production of orthopaedic products, coating of woven fabrics, material for embedding and electrical insulation, compliant with FDA 21 CFR 177.2600 and BfR-Recommendation XV „Silicones“ | A 1 slow colorless / blue A 1 rapid colorless / blue | 10 10 | white / blue white / blue | 9,000 9,000 | 120 20 | 24 16 | |