Deutsch| Product | Special features and important properties | Mixing viscosity (unfilled) mPas | Pot life unfilled | Pot life filled | demouldable 4-5 mm thickness of layer (approx. values) | demouldable 30-40 mm thickness of layer (approx. values) | castable (filled system) layer thickness* in mm (approx. values) | Data Sheet |
|---|---|---|---|---|---|---|---|---|
| MultiCast 1 hardener ISO 2 | very low casting viscosity, low shrinkage, low exothermic reaction posibility of thick layers high heat stability | 55 | 3,5 min. | 5,5 min | 45 min | 30 min | approx. 80 mm* |  |
| MultiCast 2 hardener ISO 2 | low casting viscosity good curing properties low shrinkage high heat stability | 65 | 3,5 min. | 5,5 min | 25 min | 20 min | approx. 40 mm* | |
| MultiCast 3 hardener ISO 25 | low-viscous, easy to process, low shrinkage, good through-curing, cures to be white | 80 | 2 min. | 4 min. | 15 min | 30 min | approx. 30 mm* | |
| MultiCast 4 hardener ISO 26 | low-viscous, easy to process, low shrinkage, good through-curing, cures to be white | 40 | 2,5 min. | 4 min. | 10-30 min | 20-40 min | approx. 30 mm* | |
| MultiCast 5 hardener ISO 2 | very quick-curing very high heat stability | 110 | 2,5 min. | 4 min. | 15 min | 13 min | approx. 20 mm* | |
| MultiCast 6 hardener ISO 2 | very low-viscous, very quick-curing even in thin layers | 60 | 2 min. | 4 min. | 20 min | 20 min | approx. 20 mm* | |
| MultiCast 7 hardener ISO 1 | casting system of very high quality, very high impact strength also suitable for the fabrication of plastic parts | 150 | 3,5 min. | 5,5 min | 100 min | 45 min | approx. 10 mm* | |
| MultiCast 8 hardener ISO 2 | low-viscous, easy to process, low shrinkage | 100 | 5 min. | 9 min. | 150 min | 90 min | approx. 80 mm* | |
| MultiCast 10 hardener ISO 2 | low-viscous, easy to process, low shrinkage | 80 | 2 min. | 4 min. | 20 min | 15 min | approx. 30 mm* | |
| MultiCast 11 hardener ISO 1 | casting system of very high quality, very high impact strength prototype material | 600 | 5 min. | 4 min. | 10 h | 3,5 h | unfilled approx. 5 mm | |
| PN 1515 hardener ISO 1 | medium fast-curing, low odour, very high impact strength | 350 | 5 min. | 4 min. | 3-4 h | 3-4 h | unfilled approx. 5 mm | |
| MultiCast 12 hardener ISO 2 | (fast-)casting resin long pot life very low shrinkage | 105 | 9 min. | 12 min. | 6 h | 3 h | approx. 120 mm* | |
| MultiCast 13 hardener ISO 13 | casting resin, medium-fast curing, low-odour, low-viscous, very impact resistant (after tempering) | 150 | 9 min. | n.t. (not tested) | 4 h | 3 h | approx. 120 mm* | |
| MultiCast 15 hardener ISO 3 | (fast-)casting resin long pot life relatively short demoulding time heat stability > 140 °C (filled) | 170 | 14 min. | 17 min. | 4 h | 2,5 h | approx. 150 mm* | |
| MultiCast 30 hardener ISO 1 | low viscosity long open time castable in very high thicknesses | 430 | 35 min. | 30 min | 24 h | 8 h | > 200 mm* | |
| Product | Special features and important properties | Mixed viscosity mPas | Pot life (filled) approx. | demouldable 4-5 mm thickness of layer | demouldable 30-40 mm thickness of layer | castable layer thickness* in mm | Data Sheet |
|---|---|---|---|---|---|---|---|
| MultiCast 20 hardener ISO 5 | prefilled casting system very good curing low-visvous very fine structure | approx. 2,500 | approx. 5 min | 35 min | 25 min | approx. 40 mm* | |
| MultiCast 21 hardener ISO 5 | prefilled casting system very good curing low-visvous very fine structure | approx. 1,200 | approx. 4 min | 20 min | 15 min | approx. 40 mm* | |
| MultiCast 22 hardener ISO 5 | prefilled casting system, very good curing, medium-viskous, very low shrinkage | approx. 2,200 | approx. 5 min | 30 min | 20 min | approx. 60 mm* | |
| MultiCast 23 hardener ISO 23 | prefilled casting system very good curing medium-viskous very low shrinkage | approx. 800 | approx. 5 min | 35 min | 25 min | approx. 60 mm* | |
| MultiCast 27 hardener ISO 5 | prefilled casting system, possibility of very thick layers, long open time, very low exothermic reaction, very low shrinkage | 1,500 | 90 min | 24 h - 36 h | 24 h | <500 mm* | |