RTV Silicones Condensation Systems (low strength/high strength)
NEUKASIL Condensation Systems—the Ideal Choice for Making Highly Resistant Molds.
Condensation-curing silicone compounds are the way to go whenever high efficiency and resistance to reproduction materials or casting systems are required.
Whether it’s for making molds, molding concrete, or creating artwork: The positive properties of our RTV Silicones condensation systems make them suitable for many applications. NEUKASIL RTV Silicones Condensation Systems provide molding materials that combine good flow characteristics and easy processing with high product reliability.
Condensation Systems
Our NEUKASIL RTV Silicones Condensation Systems at a glance.
| Products | Properties / field of application | Crosslinker type | Crosslinker addition % | Colour of caoutchouc | Density g/cm³ | Mixed viscosity at RT mPas | Pot life at RT min | Time required up to the demouldability hours | Tensile strength DIN 53504 N/mm² | Elongation at break DIN 53504 % | Resistance to tear propagation ASTM D 624 B N/mm | Shore A-hardness DIN 53505 | Date sheets for download |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| NEUKASIL RTV 10 |
casting- and embedding compound, very low viscosity and high shore hardness | C 1 C 5 C 25 NEU |
3 3 2-3 |
white white white |
0,9 1,0 0,9 |
4.000 4.000 4.000 |
160 80 18 |
24 15 6 |
2,0 2,0 2,0 |
150 150 150 |
4 3,5 4 |
50 50 50 |
 |
| NEUKASIL RTV 13 |
low-viscous, very good flow properties, mean hardness, variable pot lives mould making, suitable for polyester, epoxides, wax, casting of electrical component parts |
C 5 | 3 |
white |
1,0 | 7.000 | 45 | 6 | 2,5 | 200 | 4,0 | 30 | |
| NEUKASIL RTV 14 |
coating of conveyor belts, coating compound medium shore hardness | C 5 | 2 - 3 |
white |
1,0 | 450.000 brushable |
25 | 8 | 2,5 | 250 | 5,5 | 45 | |
| NEUKASIL RTV 16 |
casting- and embedding compound, low viscosity, low shore hardness | C 5 | 3 |
white |
1,0 | 5.600 | 40 | 8 | 2,0 | 400 | 3,0 | 20 | |
| NEUKASIL RTV 17 |
casting- and embedding compound, electronic potting, low viscosity, high shore hardness, temperature resistance | C 5 C 25 NEU |
2-3 2-3 |
red |
1,0 1,05 |
7.000 7.000 |
45 5 |
15 6 |
4,0 2,0 |
200 100 |
4,0 3,0 |
65 65 |
|
| NEUKASIL SN 1995 |
high resistance to initial tearing and tear propagation, very good flow properties mould making |
C 1 | 5 |
red brown |
0,9 | 9.000 | 120 | 3,5 | 130 | 2,8 | 45 | |
Condensation Systems – high strength
Our NEUKASIL RTV Silicones Condensation Systems (high strength) at a glance:
| Products | Properties / field of application | Crosslinker type | Crosslinker addition % | Colour of caoutchouc | Density g/cm³ | Mixed viscosity at RT mPas | Pot life at RT min | Time required up to the demouldability hours | Tensile strength DIN 53504 N/mm² | Elongation at break DIN 53504 % | Resistance to tear propagation ASTM D 624 B N/mm | Shore A-hardness DIN 53505 | Date sheets for download |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| NEUKASIL RTV 1703 |
high resistance to initial tearing and tear propagation, can be made thixotropic, good flow properties, for mould making and artistic casting, suitable for epoxy resins, polyurethanes, wax | 1703 Komp. B1 1703 Komp. B2 SI - C |
5 5 0,1 - 1,0 |
white | 1,22 | 24.000 32.000 |
80 15 - |
24 12 - |
4 3,5 - |
800 750 - |
>20 >20 - |
23 23 - |
|
| NEUKASIL RTV 102 |
good resistance, against resins, low shore hardness, with C 02 S short pot life | C 02 C 02 S |
5 5 |
white |
1,1 | 20.000 16.000 |
100 15 |
20 1 |
3,0 2,5 |
450 450 |
20 20 |
21 19 |
|
| NEUKASIL RTV 103 |
good resistance against resins, medium shore hardness, with C 02 S short pot life | C 02 C 02 S |
5 5 |
white |
1,1 | 37.000 48.000 |
90 15 |
20 10 |
2,5 2,5 |
420 420 |
20 20 |
28 26 |
|
RTV 102 and RTV 103 can be mixed with each other to adjust an individual Shore A-hardness. Liquid silicone ingredients can be removed by means of our NEUKASIL silicone and wax remover.
| Products | Properties / field of application | Crosslinker type | Crosslinker addition % | Colour of caoutchouc | Mixed viscosity at RT mPas | Pot life at RT min | Tack-free in hours | Shore A hardness DIN 53505 (24h) | Shore A hardness DIN 53505 (7d) | Resistance to tear propagation ASTM D 624 B N/mm | Elongation at break % DIN 53505 S2 | Data sheets for download |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| NEUKASIL RTV 125 |
high resistance to initial tearing and tear propagationt, one crosslinker each with a good resistance to styrene (C 125 PE) and a good resistance to polyurethane (C 125 PU), can be made thixotropic | C 125 PE C 125 PU SI - C |
5 5 0,1 - 1,5 |
Bernstein Creme Transluzent |
25.000 |
70 70 - |
26 26 - |
24 24 - |
28 28 - |
22 22 - |
800 650 - |
|
| NEUKASIL SN 1971 |
high resistance to initial tearing and tear propagation, very good flow properties mould making |
C 02 C 04 |
5 20 |
Weiß |
9.000 4.000 |
95 60 |
24 |
13 10 |
15 11 |
19 4 |
370 420 |
|
You are interested in our NEUKASIL
RTV Silicones and would like
a personal consultation?
Arrange a consultation now: +49 (0)451 499 600
Speed and flexibility
Expect high availability and speed, because we are as dynamic as the markets we serve.
Reliable availability of our products and speed in order processing are crucial to the success of our system and raw material customers.