ProtoCast

ProductSpecial featuresMixed viscosity (unfilled)
mPas
Pot life (unfilled)demouldable
4-5 mm
thickness of layer */**
castable layer thickness
in mm***
Data Sheet

ProtoCast 100-05


ProtoCast 100-15

very good impact strength, excellently dyable, variable pot lifes2204 - 6 min


14 - 16 min
30 - 40 min2 - 7 mmBild-Merkblatt
Bild-Merkblatt
ProtoCast 102
hardener comp. B
very good impact strength, excellently dyable, white after curing, high HDT3955 - 6 min30 - 60 min2 - 7 mmBild-Merkblatt
ProtoCast 103 hardener comp. Bvery good impact strength, excellently dyable, translucent-white after curing, high HDT4504 min30 - 60 min2 - 5 mmBild-Merkblatt
ProtoCast 105 hardener comp. Bvery good impact strength, excellent dyable, white after curing, high HDT3255 - 7 min30 - 60 min2 - 7 mmBild-Merkblatt
ProtoCast 110
hardener PTG 1
hardener PTG 4
very good impact strength, prototype material similar to ABS500
600
4 min
4 min
60 -75 min
60 -75 min

2 - 10 mm (unfilled)
2 - 10 mm (unfilled)

Bild-Merkblatt
ProtoCast 112 hardener PTG 8very high impact strength, short pot life and short demoulding time prototype material (similar to PP)5002 min5 - 15 min2 - 7 mm (unfilled)Bild-Merkblatt
ProtoCast 113
hardener PTG 1
hardener PTG 4
high impact strength, short pot life and short demoulding time, high heat stability / prototype material (similar to ABS and PP)400
450
3 min
3 min
20 - 30 min
20 - 30 min
2 - 7 mm (unfilled)
1 - 7 mm (unfilled)
Bild-Merkblatt
ProtoCast 115
hardener PTG 1
hardener PTG 4
good impact strength, short pot life and short demoulding time, very high heat stability800
1000
4 min
4 min
30 - 60 min
30 - 60 min
2 - 7 mm (unfilled)
2 - 7 mm (unfilled)
Bild-Merkblatt
ProtoCast 120
comp. B 1
comp. B 2
excellent impact strength, high dimensional stability under heat, very good flowability, suited for: prototyping, small lot production and production of technical parts750
530
approx. 6,5 min
approx. 6,5 min
30 - 60 min
30 - 60 min
2 - 8 mm
2 - 8 mm
Bild-Merkblatt
ProtoCast 120 GF
comp. B 1
comp. B 2
excellent impact strength, high dimensional stability under heat, very good flowability, suited for: prototyping, small lot production and production of technical parts---3 - 5 mm
3 - 5 mm
Bild-Merkblatt
ProtoCast 140
comp. A/comp. B
similar to ABS, high heat stability, quick curing1200approx. 7 min45 - 60 min2 - 7 mmBild-Merkblatt
ProtoCast 195
comp. A/comp. B
transparent (not UV stable), very good flowability, quick curing800approx. 5 min15 - 30 min2 - 7 mmBild-Merkblatt
ProtoCast 229
comp. A
comp. B
properties similar to those of PMMA transparent, colourless, very good resistant to yellowing, high thermal stability, very quick-curing, mercury-free110 approx. 3,5 - 6 min1-3 mm: 60 - 120 min1 - 3 mmBild-Merkblatt
ProtoCast 229-10
comp. A
comp. B
properties similar to those of PMMA transparent, colourless, very good resistant to yellowing, high thermal stability, very quick-curing, mercury-free110 approx. 10 min1-3 mm: 60 - 120 min1 - 3 mmBild-Merkblatt
ProtoCast VZ****prototype material (ABS), Prolongation of the pot lives of ProtoCast systems, decrease of exothermic reaction, higher thicknesses possibleonly in combination with e. g. PC 115 usablee. g. + 25 % to PC 115: 7 - 8 min30 - 45 min5 - 15 mm (unfilled)Bild-Merkblatt

*     room temperature
**    after storage at 70 - 80°C/thickness of layer approx. 5 mm
***  castable layer thickness of filled (width: approx. 20 - 30 mm) and unfilled systems constitutes a recommendation and partially depends on the geometries of parts to be moulded. The statements of this data sheet serve the information only and are legally not binding.
**** mixing ratio of ProtoCast VZ with PTG 1 and PTG 4 see data sheet.

Protocast products are sold unfilled and can be formulated individually by adding certain fillers.

NEUKADUR Prototype Resins rigid and/or viscoplastic

cured 1 day at room temperature / 1 - 2 hour 80 °C

ProductProperties (similar to)Mixing ratioMixing viscosity mPasPot life minutes approx.Hardness Shore-DHeat stability °C (2 - 5 mm) (unfilled)Tensile strength
DIN 53455
Elongation % DIN 53455Flexural strength
N/mm² DIN 53452
Bending Elongation % DIN 53452Flex. mod. of elasticity N/mm²
DIN 53457
Impact strength
KJ/m² DIN 51230
ProtoCast 100-05 ProtoCast 100-15 hardener comp. BABS100:100
100:100
320
320
4 - 6
15 - 20
80
80
80
80
47
47
18
18
69
69
7
7
1,605
1,605
20
20
ProtoCast 102 hardener comp.. BABS30:1003955 - 6789578-61-1,60025
ProtoCast 103 hardener comp. BABS50:100450480100681692-2,35030
ProtoCast 105 hardener comp. BABS50:1003255 - 782105711599-2,30035
ProtoCast 110
hardener PTG 1
hardener PTG 4
PP / HDPE100:100
100:85
500
600
4
4
77
80
75
85
42
48
18
16
70
65
15
12
1,200
1,400
>55
50
ProtoCast 112 hardener PTG 8PE/PP100:75500278ca. 6525183223460100
ProtoCast 113 hardener PTG 4ABS100:100 45037880 - 85481972101,20031
ProtoCast 115
hardener PTG 1
hardener PTG 4
ABS
ABS
100:120
100:100
800
1000
3 - 4
3 - 4
82
83
80-110
100-110
53
60
15
13
100
105
9
9
1,700
1,750
26
25
ProtoCast 120
Comp. A/ comp. B 1
Comp. A/ comp. B 2
ABS/PA
ABS/PA
65:100
65:100
750
600
6,5
6,5
84
84
110-120
ca. 130
55
60
28
25
100
105
15
13
1,500
1,700
60 - 80
40 - 80
ProtoCast 195 comp. A/ comb. Btransparent70 - 100800580ca. 906421110121,90060